Product Details:
|
|
Place of Origin: | CHINA |
---|---|
Brand Name: | GUIBAO |
Certification: | ISO, SIRIM |
Model Number: | 1092 |
Payment & Shipping Terms:
|
|
Minimum Order Quantity: | 10 kits |
Price: | Negotiable |
Packaging Details: | Part A:190L part B:19L |
Delivery Time: | 4 working days |
Payment Terms: | T/T |
Supply Ability: | 100 kits/4 working days |
Detail Information |
|||
Features: | Two Parts , Neutral Cure | Usage: | Construction |
---|---|---|---|
Color: | Black After Mixing | Shelf Life: | 12 Months |
Application: | Structural Sealing And Glazing Of The Curtain Wall Of High-rise Buildings Or Skyscrapers. Structural Sealing And Glazing In Large-sized Glass Panel Curtain Walls | Quality: | High |
Basic Uses: | Structural Sealing And Glazing | ||
High Light: | heat resistant silicone sealant,clear silicone sealant |
Product Description
High Performance Silicone Structural Glazing Sealant for High Rise Building
TYPICAL PROPERTIES
These values are not intended for use in preparing specifications.
Test Method | Property | Unit | Standard | Result |
GB/T 13477 (ISO 7390) | Slump | mm | ≤3 | 0 |
GB/T 13477 (ASTM D 2377) | Tack free time | h | ≤3 | 01 |
GB/T 13477 | Working time (after 20 min.) | s | ≤10 | 2.4 |
GB/T 531.1 (ISO 7619) |
Hardness | Shore A | 30~60 | 40 |
GB 16776 (ASTM C 792) | Heat Aging | |||
weight loss | % | ≤10 | 3.3 | |
cracking | Nil | Nil | ||
chalking | Nil | Nil | ||
GB/T 13477 (ISO 8339) | Tensile strength |
MPa |
||
at 23℃ | ≥0.6 | 1.35 | ||
at 90℃ | ≥ 0.45 | 1.01 | ||
at -30℃ | ≥ 0.45 | 1.85 | ||
water immersion | ≥ 0.45 | 1.21 | ||
water-UV exposure | ≥ 0.45 | 1.18 | ||
adhesion failure | % | ≤ 5.0 | 0 | |
elongation at ultimate tensile strength at 23℃ |
% | ≥ 100 | 201 |
*GB: Chinese National Standard
ASTM: American Society for Testing and Materials
ISO: International Standardization Organization
FEATURES
Two parts , neutral cure to form an extremely tough elastomeric rubber ensuring a durable, flexible, and watertight bond.
High level of mechanical properties , high tensile strength and extension rate.
Excellent weatherability and high resistance to ultra-violet radiation ,heat and humidity, and ozone.
Excellent stability over temperature range from –50 ℃ to +150 ℃.
Excellent unprimed adhesion to a wide range of substrates.
Good compatibility with other neutral silicone sealants.
COLOURS
Part A(base) of GB 1092 is available in white, part B(curing agent) in black. Black colour after mixing.
PACKAGING
GB 1092 is available in kit: Part A in 200Ldrums (net 190L), part B in 20L pails (net 19L).
BASIC USES
GB 1092 High Performance Silicone Structural Glazing Sealant is designed for:
Structural sealing and glazing of the curtain wall of high-rise buildings or skyscrapers.
Structural sealing and glazing in large-sized glass panel curtain walls.
SPECIFICATIONS
GB1092 is designed to meet or even exceed the requirements of:
Chinese national specification GB16776-2005 Silicone Sealant for Structural Glazing.
Complies with ASTM C 1184.
STORAGE AND SHELF LIFE
GB1092 should be stored in original unopened containers. It has a shelf life of 12 months from the date of manufacture.
LIMITATIONS
GB1092 should not be applied:
To the materials that bleed oils , plasticizers or solvents, such as impregnated wood, oil-based caulks.
In totally confined spaces as sealant requires atmospheric moisture for cure.
To frost laden or damp surfaces.
For continuous water immersion.
When substrate surface temperature below 4℃ or over 50℃.
HOW TO USE
Surface Preparation
Clean all joints removing all foreign matter and contaminants such as oil, grease, dust, water, frost, old sealants, surface dirt, or glazing compounds and protective coatings.
Mixing and Dispensing
To obtain the optimal performance of GB 1092, it is recommended that base and curing agent thoroughly mixed using an airless two-part silicone dispensing machine.
GB 1092 should be mixed at a ratio of 9:1~11:1 base to curing agent by volume or 11:1~13:1 base to curing agent by weight.
Lot matching of GB1092 base to curing agent is not required. Before use, it is recommended that curing agent be fully stirred to ensure the homogeneity of all components.
GB 1092 part B curing agent will react with atmospheric moisture, therefore should not be exposed to air for prolonged periods of time.
Priming
Priming is not usually required when using GB 1092.But it is essential that adhesion is tested prior to use to decide whether to use primer or not.
Masking and Tooling
Areas adjacent to joints may be masked to ensure a neat sealant line. Do not allow mask tape to touch clean surfaces to which the silicone sealant is to adhere. Tooling should be completed in one continuous stroke after sealant application. Masking tape should be removed immediately after tooling.
Equipment Cleaning
When not being used, it is recommended that the dispensing equipment be purged either with the base component or flush with suitable solvent.
SAFETY INFORMATION
GB 1092 is a chemical product, not edible, no implantation into body and should be kept away from children.
Cured silicone rubber can be handled without any risk to health.
Should uncured silicone sealant contact with eyes, rinse thoroughly with water and seek medical treatment if irritation persists.
Avoid prolonged exposure of skin to uncured silicone sealant.
Good ventilation is necessary for work and cure places.
TECHNICAL SERVICES
Complete technical information and literature, adhesion testing and compatibility testing are available from Guibao.
DISCLAIMER
The information presented herein is offered in good faith and is believed to be accurate. However, because conditions and methods of using our products are beyond our control, this information should not be used in substitution for customer’s tests to ensure that our products are safe, effective, and fully satisfactory for intended specific uses.