Elastomer Chimney Anti Corrosion Coating / Excellent Anti Corrosion Paint

Product Details:
Place of Origin: CHINA
Brand Name: GUIBAO
Certification: /
Model Number: 1077
Payment & Shipping Terms:
Minimum Order Quantity: 50 sets
Price: Negotiable
Packaging Details: Part A as 20kg/plastic pail, Part B as 2.5L(1.4kg)/metal pail
Delivery Time: 5 working days
Payment Terms: T/T
Supply Ability: 500 sets/ 5 working days
  • Detail Information
  • Product Description

Detail Information

Color: Part A Is Black, Part B Is Yellow, And The Mixture Is Black Shelf Life: 12 Months
Packing: Part A As 20kg/plastic Pail, Part B As 2.5L(1.4kg)/metal Pail Key Words: Anti-corrosion Material,chimney
Feature: Two Part,Excellent Corrosion Resistance For Withstanding The Corrosion Damage Of Various Strong Acid And Alkali At Higher Temperatur Quality: High
High Light:

anti corrosion protection


heat resistant adhesive

Product Description

Elastomer Anti-corrosion Material Chimney Anti Corrosion Coating


Guibao 1077 elastomer anti-corrosion material is an acid and alkali resistant and high temperature resistant elastomer anticorrosive material specially developed for the lining anticorrosion of thermal power plant chimney, sewage treatment tank, chemical treatment tank, etc. The product has passed the appraisal of China Electricity Council (CEC) and is rated as a product technology innovation, with independent intellectual property rights, reaching the international advanced level, in which corrosion resistance has reached the international leading level. It can be used as the lining base protection layer and widely used in the lining anti-corrosion engineering for coal-fired chimney, sewage treatment plant, chemical plant, power plant, etc.


Product Features


Two parts, room temperature curing;

Excellent elasticity for adapting to the thermal expansion and contraction stress of various substrates after curing without cracking and falling off;

Excellent corrosion resistance for withstanding the corrosion damage of various strong acid and alkali at higher temperature;

Good permeability and wear resistance for resisting the scouring and permeability of fluid, such as flue gas dust and high flow rate gas;

Good resistance to high and low temperature for long-term use below 100 °C and short time service at 120~150 °C after curing;

Good adhesion to concrete, acid-resistant brick, steel base, FRP, ceramic, etc., with wide application range;

No harmful gas volatilization, no harm to the human body, and no pollution to the environment.


Main Usage


Lining anti-corrosion of chimney, gas flue, cooling tower, etc., in the thermal power plant;

Lining anti-corrosion of sewage treatment systems, such as concrete sewage tank, steel tank, etc., in the sewage treatment plants, chemical plants, power plants, etc.

External corrosion protection of pipes, metal structural components, etc.


Typical Technical Indicators (the measured values should not be considered as product standards)






Standard Requirement

Performance Indicators

Test Method


Tack-free time

H ≦3 2.0 GB/T 13477.5

Pot life

Min ≧60 68 GB 16776

Shore hardness

ShoreA 40~70 48 GB/T 531.1

Mechanical properties


Tensile strength

MPa ≧2.0 2.5 GB/T 528

Elongation at break

% ≧100 182

Acid resistance

(50 ° C mixed acid × 14d)

Tensile strength retention

% ≧80 92

Retention for elongation at break

% ≧80 83

Heat resistance

(120 ° C × 24h)

Tensile strength retention

% ≧90 104

Retention for elongation at break

% ≧70 93

Bond shear strength

MPa ≧1.0 2.5 GB/T 7124


The mixed acid ratio (mass fraction) is 9.5% sulfuric acid, 0.5% nitric acid, 0.1% hydrochloric acid, and 0.01% hydrofluoric acid.


Application Method


Before application, the surface of the substrate should be polished and cleaned to avoid affecting the bonding;

Add Part B into Part A according to the manufacturer's recommended ratio after its uniformly stirring;

Mix Part A&B uniformly and then evenly spread on the substrate with a tool.




Part A is black, Part B is yellow, and the mixture is black.





Part A as 20kg/plastic pail, Part B as 2.5L(1.4kg)/metal pail;

Recommended mixing ratio: A: B = 14~16:1 (mass ratio)




Net content: Part A as 20kg, Part B as1.4kg;


Executive Standard







Store in a cool, ventilated and dry place . From the date of production, the storage period is 12 months in the unopened &sealed container.




Transported as non-dangerous goods




Not suitable for frosted or wet substrate surfaces;

When the surface temperature of the material is lower than 5 °C or exceeds 50 °C, it is not suitable for application;

Part A&B should be thoroughly mixed to avoid unevenness and affect the performance of the elastic material;

Part A&B should be stored separately, and prepared when using; after preparation, it should be used within the specified time to avoid waste;

Before bonding the relevant substrate and mass-scale application, the adhesion should be checked in advance;

Uncured adhesive should not be in contact with the skin for a long time. In case of eyes contact, rinse with plenty of water and seek medical advice immediately;

This product is a chemical product, and forbidden to eat and to be implanted in the body; keep the uncured product away from touch of children.